Bio-degradable poly (l-lactic acid) (PLLA) scaffolds were prepared by using thermally induced phase separation (TIPS) method. A solution of PLLA-Dioxane was formed by dissolving PLLA in dehydrated 1,4-Dioxane at three wt/vol percentages, specifically 3, 7 and 10%. This PLLA-Dioxane solution was then frozen in borosilicate glass vials (5mL) at three cooling rates (1, 10 and 40 ˚C/min) in a commercially available controlled rate freezer (CRF). The frozen solution was freeze-dried to sublimate the Dioxane. The microstructural properties of the resulting PLLA scaffolds were determined utilizing Scanning Electron Microscopy (SEM) images and uni- axial compressive testing. The relationship between the wt/vol ratio of PLLA and Dioxane and the imposed cooling rates on the structural properties of PLLA scaffolds was determined. This same procedure was then repeated using a mixture of Dioxane and Ethanol. The volume of the mixture constituted 15% of Ethanol and 85% Dioxane.

Date

2013

Document Availability at the Time of Submission

Secure the entire work for patent and/or proprietary purposes for a period of one year. Student has submitted appropriate documentation which states: During this period the copyright owner also agrees not to exercise her/his ownership rights, including public use in works, without prior authorization from LSU. At the end of the one year period, either we or LSU may request an automatic extension for one additional year. At the end of the one year secure period (or its extension, if such is requested), the work will be released for access worldwide.

Committee Chair

Devireddy, Ram

DOI

10.31390/gradschool_theses.2634

Download

Share

COinS