The electrodeposition of nickel-rhenium alloys from Ni(II) and Re(VII) solution was studies in an aqueous acidic solution. Different plating current density and pH have been carried out, and the effect of them on the composition of the deposited Ni-Re alloy was studied. Wavelength-dispersive spectrometer (WDS) was used to measure the composition of Ni-Re alloy. The thermal stability of nickel-rhenium alloy system has been investigated. Differential scanning calorimetry (DSC) tests have been conducted for the electroplated Ni-Re samples in order to find the possible heating initiated interactions at elevated temperatures. To investigate the thermal stability of Ni-Re alloys, the samples were annealed under nitrogen environment for 90 minutes at 280°C, 350°C, 600°C and 900°C. Transmission electron microscopy (TEM) was used to exam the microstructures of Ni-Re alloy samples as-deposited and heat-treated. The results show that the as-deposited Ni-Re material grain size for this plating condition is around 380nm. The results also show that after heating at 600°C for 90 minutes, there was no significant grain growth observed. The microhardness and nanohardness of Ni-Re alloy were also studied with as-deposited and heat-treated samples. Tensile strength was carried out by dynamic mechanical analyzer (DMA) at room temperature and elevated temperature of 400°C. This research demonstrated a well developed, thermally stable and mechanically sound material system for LIGA/MEMS high temperature robust applications.

Date

2005

Document Availability at the Time of Submission

Release the entire work immediately for access worldwide.

Committee Chair

Wanjun Wang

Share

COinS